  1. All we need to do is arrange a time on a weekend at the BGOP shop, Chris. Doesn't matter if your membership has expired; mine is still active. And I probably know a couple guys who'd jump at the invite.
  2. One note to add is that recalescence (the opposite effect on the way down) happens at a cooler temperature than recalescence. So you really need to catch it on the way up. If you catch it on the way down the blade is cooler than you want it for quenching.
  3. When I first read this over at IFI, I couldn't quite get it to register for just the reason you mentioned, Alan. Just Friday or Saturday he'd mentioned something in a post that I spent an hour or so this weekend trying to look up. I meant to ask him about it. Grant knew so much about so many things that we'll never really know everything he took with him. There was an update on the NWBA site last night that mentioned it was an aortic aneurysm.
  4. I've tried DIY mixes, and none of them are as easy or as pleasant to work with -- or probably as durable, for that matter -- as the commercial stuff. Portland loses its bonding power at high temps as it dehydrates. The offgassing of steam can cause explosive spalling, although it won't necessarily do so -- e.g., if the Portland content is low and the matrix is porous. Still, beyond a certain point it isn't contributing any bonding power, although it may help flux the surrounding ceramics to get them to sinter at a lower temp. Too much Portland will cause serious fluxing problems and reduce the
  5. Thanks, Greg. Those are interesting links, and some of those threads contain other interesting links as well. The pic at the top of the last link you provided looks very similar to this knife in terms of overall shape, the shape of the blade, the decorations on the brass, etc.
  6. Thanks for the tip, JD. I sent Mr. Levine an email. And yeah, I noticed that it's pretty navaja-like.
  7. Matt Bower

    old folder

    This knife has been in my family for a long time, and this weekend I finally got around to taking a few photos. My grandfather looked into the history of the blade a bit, many years ago, but unfortunately no one wrote down what he found. I have a vague recollection that he decided it was probably made in Philadelphia in the late 18th or early 19th century, but I could be mistaken about all of that. I'd welcome any info that any of you folks can provide, particularly if anyone recognizes the maker's mark. Please don't ask why I didn't take a pic with the blade locked fully open. I have no expla
  8. You can get 1000 grit from ceramics suppliers like Bailey. I don't know where you'd get 1500. I'm sure it's out there somewhere, though. Good luck.
  9. I was sorry to hear of this. Growing up during the late Cold War, I considered men like Vaclav Havel and Lech Walesa heroes. Perhaps a little crazy, I thought at the time (now I realize "very brave" would have been a better description), but certainly heroes.
  10. You could grind one straight edge on it, a couple inches long. That'd probably do. It wouldn't require too much work with an angle grinder, and you wouldn't have to (or want to) flatten the side of the anvil for its entire length -- you'd only need to grind a couple inches down from the face. A longer straight edge would be more convenient, but you don't have a lot of material to play with. Upsetting the face and squaring it by forging would probably work well, too, but it'd be a lot of work and you'd need at least one helper (human or machine). I don't know if you could successfully harden th
  11. Unless you're going to be running your burner outside the forge, you generally don't need a separate flare. Just build the flare into the forge itself, as Brian suggested.
  12. The breaker hammer bits that I have are within the range for 1045, as Alan said, and as described in that link above. Grant Sarver suggested they might be something like 15B40, which is .4% carbon with a tiny amount of boron to improve hardenability. (He used to make these bits and had a bunch of his competitors' products tested.) That could be; the boron content in 15B40 is so low that it might have been written off as "trace" on the test results I got. (My bits don't have enough Mn to be 15B40, but they could be a similar proprietary alloy.) For $5 each, they're probably worth buying. Wi
  13. Pretty sure lots of folks here use them. I just recently bought one and am likely going to be trying it out very soon.
  14. If I had paid for that, I would be annoyed. The workmanship is crude, the design frankly doesn't look very efficient and, to top it all off, it was defective! (That probably relates back to the crude workmanship, but there's a difference between "crude but effective" and "crude and dangerous.") It might not be a bad idea to pressurize the orifice assembly in a sink or basin full of water, to check for any other leaks. (You could use air rather than propane.) You can also do it by brushing on a soapy water solution.
  15. I don't know if I've ever seen that kind of flame out of a propane burner. Like a couple others before me, I'm wondering if your regulator is providing enough pressure. And do you know (or can you find out) what size the propane orifice is?
  16. I've only had it backfire out the ash dump. That's unnerving.
  17. I think he meant that Kazda still gets his royalties if you download the video from Amazon On Demand. You are quite right about YouTube, of course.
  18. It's technically not theft, but copyright infringement. It generally isn't a criminal offense except with the addition of some specific aggravating factors. However, statutory damages in civil cases are up to $30,000 per work infringed, $150,000 in cases of willful violations, plus the other guy's attorneys' fees. And on top of that, as already suggested, copyright infringement takes money out of the pockets of people who create valuable works. Make it unprofitable and they might just stop producing. Then we'd all be much worse-off.
  19. I made an anvil out of 1" thick plates about 20" long and 10" wide, stood on end, heavily chamfered, and welded all around. Then I welded a piece of plate to the top and hardfaced it. It wasn't great, but it was better than a piece of 3/4" plate welded to the end of a chunk of i-beam, which is what I started with.
  20. The adobe forge was Tim Lively's. Sadly, Tim shut down his website a while back, after he quit bladesmithing. I don't think it had anything to do with that forge not working well. I sometimes make a little firebrick enclosure over the firepot of my coal forge, for heat treating. Similar concept to this, but less permanent.
  21. My quench tank for blades is an artillery propellant canister that I bought at a gun show for like $10.
  22. In the unlikely event that your oil catches fire (assuming you're using oil), a metal bucket with a lid can easily contain and smother the fire. Plastic could be more of a problem. That said, I once accidentally dropped a big chunk of bright orange leaf spring into a 5 gallon bucket of water. It did not melt through the bottom. Leidenfrost effect, I assume. (It did ruin the steel.)
  23. By the way, you don't actually have to liquefy borax to dehydrate it. Baking it in the oven at 550 F for about three hours will convert it to over 90% anhydrous borax. It's pretty solid after that, but I suspect it's still a little easier to grind than the stuff that's been fused. (I've never messed with the stuff that's been fully melted, so I don't know that for sure.)
  24. It's good to know that someone actually uses 20 Mule Team for laundry. I thought blade/blacksmiths were the only people keeping those guys in business.
  25. That doesn't sound like a normalizing problem. It sounds like overheating, or a problem with the steel.
×
×