  1. Thank you for the advise . yes indeed its too hard.
  2. Dear Sir, Yes I have sent that SKD 11 block for heat treatment and air hardening. The steel SKD 11 after treated gets 60 hrc and its dam hard. But i am not pro at forging and didnt test to forge any thing.The anvil is for my bladesmith fucture use.total for this item cost me USD 400. Thank for reply
  3. Dear ALL, I am mohd from malaysia would like to get some information regarding SKD 11 steel. I have baught 6x6x10 inch of skd 11 steel to make an anvil. Do any body here know weather this steel have a potential for forging purpose.Please advice. Thanks
  4. Dear Sir, Can anybody guide me on buying Japanese Forging machine for making knife. Thank You
  5. SEPOH

    Hamon

    Dear Members, Do any of the members has tried to use this clay mixing for tempering any kind of knife/sword.Let us see the hamon if there is a result and what is the ratio for the mixing. Best Regards Sepoh
  6. Dear R Harrell, Do Read My Posting Regarding clay mixing in Hamon topic. Thats is the real receipie which use in japanese HT for blades.The only missing is the RATIO of the mix. Regards Sepoh
  7. SEPOH

    Hamon

    Dear Sir, Please let us know the result and this is Full Recipie ,But The ratio They will naver open the secret.I am sure we will find the truth ratio just by experiment.AMEN. Regarding previous post I have mention Boric Acid But There is another Japanese Master Recipie which use HORIC ACID rether than BORIC ACID.I mention to him twice regarding BORIC ACID OR HORIC ACID, but he keep telling me its HORIC ACID this is why I have post earlier to this forum, what is the different between Boric Acid And Horic Acid. Powered Charcoal(Very2 Black) which is very high quality from japan use
  8. SEPOH

    Hamon

    Dear Sir, Do Anyone in this forum can explain the different between Boric acid and Horic Acid. Best Regards Sepoh
  9. Hi R.Harrell, Perhaps This link Will Guide you to a simple forge setup. www.twinoaksforge.com/BLADSMITHING/bladesmith home.htm Best Regards Sepoh
  10. SEPOH

    Hamon

    Daker, I have ask my friend she is japanese and has connection with a Japanese Bladesmith master.She mention Boric Acid,Graphite and Red Clay from Mountain But mixing the Compound is a big secreet where she did not know and just the master do it for tempering the blade. There is also tip which is helpfull ,First they coate all the blade with the mixing,Than the ashi line, The last coate is the back of the blade(mune),Either one of this 3 step they add IRON OXIDA which might be KANAHADA.I Realy Dont know why, maby experd in this forum can share the experience with the biginners.
  11. SEPOH

    Hamon

    Dear Sir, I am very please if Master Don with experd forum mambers do a experiment to Use The Boric Acid mix with best formula and tampeered one simple knife to show us the begineers, how the HAMON looks and if success we can actually just buy the Mixing compound from this forum admin.It will actually safe the time consuming and just concerntrate how to lay down the mixing compound to get BEST Hamon Pattern. Also By this experiment, (senior forum mambers) can actually get a idea weather to include or just ignore using BORIC ACID as immenint Recipie. My appologiest of asking to
  12. SEPOH

    Hamon

    Dear Sir, Its no use for you to scrap his word but to find the true is more important.Japanese master naver lie and if you have fail after the try than explaination is nacessary. If you cant see the shape of the SUN with your naked eye than you have to beleive what experd say. Dont jump to conclution easily without trying. No Joke Bro.
  13. SEPOH

    Hamon

    Hi There, I am Nuar From malaysia,I am not relly active in this subject but its my hobby to see hamon get batter over the time. Can anybody figure out and try to use BORIC ACID to mix with clay for creating Hamon.I am sure this is true solution which i have been told by a master that one of the ingredian for making the clay for tempering the sword is BORIC ACID. What i am asking is for the prefection of hamon. Please do try the mix of boric acid. Thank You Nuar
×
×