  1. Matthew, I can't thank you enough. I'll head back to the shop as soon as I can - hopefully this time I'll emerge victorious Thanks again!
  2. Greetings, gentlemen. I recently tried to do the stainless Damascus for the first time. In my blacksmithing master's shop (not having my own yet) we followed instructions by Ariel Salaverria to the letter (http://www.aescustomknives.com/docs/tutorial16.htm). On the first attempt, the container burned through after several minutes, hence the stacked steels were too cold to weld. We thought that perhaps the temperature was too high or there was too much WD40 inside. Hence, on the second attempt we put paper soaked in WD40 only on one end of the container and we poured out WD40 after squeezing it inside. We also started with slightly lower temperature. Result - after several minutes the container exploded, scattering burning coke around the shop. Luckily, nobody was injured and the shop didn't catch fire, but it wasn't very nice. Please see the attached picture of container after it was recovered. Any ideas how to do it properly? Is there any other way to do stainless Damascus in the forge? It is a simple coke-burning forge. Many thanks!
  3. Greetings, gentlemen. Apologies for my late reply. Here's some more information: - the hammer is KA-75 (http://www.ka75.com/) - the foundation was a pit 1 meter deep (about 3,3 feet), about 1x1 meters wide. - the pit was filled with cushioning materials - bottom 30 cm are from thick rubber plates, then 50 cm of thick cork plates - the sides of the pit were cushioned with Nobasil (kind of isolation used in Slovakia) - all of it was then fixed in concrete and the hammer was bolted to the floor Does that help? Many thanks!
  4. Greetings, gentlemen. One important question for you, please: My bladesmithing master installed power hammer in his shop - the type embedded in the floor in a deep pit, with proper cushioning (as per instructions). However, when it's put to work, the entire house is shaking - and since it's fairly old house, the end result is that he is unable to use the power hammer at all. It was quite costly, so we're trying to figure out what else can we do to be able to use it. Recently, my master came across notion of some kind of "pneumatic absorption pillows", that could possibly solve this problem. Do any of you, please, have some idea about what might help or where I might get pair of these "pillows"? The desired size is 28x28 cm (that would be about 11x11 inch). Any info and help is much appreciated! Many thanks, Tomas
  5. Hello all, one question regarding stainless Damascus, please. I'm going to try my hand at creating my first billet of stainless Damascus this weekend according to the method described by Ariel Salaverria (his site is unfortunately down at the moment.) I have two steels - N695 and 1.4116. From what I gather this should be very similar to what Markus Balbach uses. The important question is - what happens with the square tube used as a container for the steels? My guess is that it will weld to the steels and have to be ground off, right? Many thanks for your replies, any & all input is much appreciated. Tomas
×
×