Forgive the crude drawing, but a friend had an idea. Because oil and water separate, would it be possible to quench through the oil into the water very quickly then pull the blade back into the oil and out. My friend had fairly decent success going quickly into a bucket of water and then into a tank of oil. I realize that it would probably depend on the steel, but what do you think this process could potentially do for a blade. I am fairly new to bladesmithing and only just completed my first pattern welded piece. I would imagine that the forces of both mediums would create different forces on the steel. would it increase/ decrease warping? I would love to hear your thoughts.