      Use your real name or you will NOT get in.  No aliases or nicknames, no numerals in your name. Do not use the words knives, blades, swords, forge, smith (unless that is your name of course) etc. We are all bladesmiths and knifemakers here.  If you feel you need an exception or are having difficulty registering, send a personal email to the forum registrar here.  
DaveJ

温胡知新 (classical tanto project)

12 posts in this topic

A true and accurate understanding of the past is an important step towards a good future. 温胡知新 (on ko chi shin) is an expression that most directly translates to, "study the old to know the new". This blade began as a reclaimed piece of a damaged antique sword and was carefully hand forged in a charcoal fire, smoothed with files and a sen scraper, differentially hardened using traditional water quench yaki-ire, and polished by hand with natural Japanese water stones.

Materials for the chisagatana style koshirae mounting include Japanese hounoki wood for the handle and scabbard, copper bus bar for the habaki, reclaimed brass from the original mount for the fuchi and kojiri, forged brass kick plate for the kashira and seppa, black lacquered samegawa and kangaroo leather for the tsuka, lacquered steel for the mekugi, buffalo horn for the koiguchi and kurikata, and an iron spike salvaged from thirty feet under the Pacific for the tsuba. The saya is finished with ishime-ji (stone surface) made from natural urushi lacquer and tea leaves, the kurikata was carved from reclaimed horn button rescued from a vintage coat, and the sageo cord comes from an outdoor antique market in Kyoto.

koto-tanto-47.jpg

koto-tanto-45.jpg

Specifications

長さ/刃長 Nagasa: 11 sun 3 bu (341mm)
元幅 Motohaba: 8 bu 5 rin (25.5mm)
重ね/元重 Motokasane: 1 bu 5 rin (4.2mm)
反り Sori: uchizori
中心/茎 Nakago: 3 sun 6 bu (109mm)
柄長 Tsuka: 4 sun 5 rin (123mm)
拵全長 Koshirae: 18 sun (545mm)
形 Katachi: hira-zukuri, iori-mune
刃文 Hamon: hoso suguha
帽子/鋩子 Boshi: yakitsume
中心/茎 Nakago: futsu, suriage, one mekugi-ana, mumei
銘 Mei: mumei
拵 Koshirae: chisagatana, issaku

3.03022 cm = 0.1 shaku(尺) = 1 sun(寸) = 10 bu(分) = 100 rin(厘)

More photos and info: islandblacksmith.ca/2017/08/on-ko-chi-shin-tanto/

Edited by DaveJ
1 person likes this

Share this post


Link to post
Share on other sites

Wow. This turned out beautiful. I enjoy your videos on youtube as well. Is there going to be one of this?

Share this post


Link to post
Share on other sites

@ScottWright i needed to get it done with a deadline along with some other projects so no videos, only a few photos (more on the website)...but a professional crew came by for some footage of the forge and documented the final assembly so it should be part of a video in the future...

koto-tanto-36.jpg

islandblacksmith.ca/2017/08/komorisan-back-in-the-forge/

 

Edited by DaveJ

Share this post


Link to post
Share on other sites

Wow! I love how clean your work is. What did the sword look like before you worked on it? Did you have to forge a new tip on the old blade?

Share this post


Link to post
Share on other sites

@Wes i just added a "before" photo to the page...the antique blade had lost its hamon (likely damaged by fire) and then was abused, poorly reshaped (polished with a belt sander?), bent, and severely damaged for several inches above the hamachi..this tanto is made from the front half, i may get another tanto out of the rest in the future...

so i forged it from shinogi-zukuri to hira-zukuri and forged a tang to maximize use of the steel...delicate work but worth the effort...
 

Share this post


Link to post
Share on other sites

That steel is very very lovely.  Beautiful work David. I would imagine that the original smith would be happy to know his work was "saved" and had new life breathed into it.  I have never been struck by the need to used reclaimed materials, but I understand why you do. This knife is a testament to that.  Cheers to you

Share this post


Link to post
Share on other sites

@Wes much appreciated...indeed, redemptive art... ^____^

Share this post


Link to post
Share on other sites

Dave,

   Thanks for the tutorial, beautifully done,as was the tanto. Could you not have re-quenched that blade and started over assuming the carbon content is still there. I had a chance to see ( and touch ) some of your work in the gallery ( Coombs ) , beautiful work.. Had a wonderful chat with the gallery owner. I found myself in the area and used a phone to look at your site to find the gallery.

Jan

Share this post


Link to post
Share on other sites

@Jan ...nice! next time let me know when you are in town! that was one approach i considered, but there was too much damage to the blade, particularly to the edge for several inches above the machi...so it would have been a suriage wakizashi at most, however there was some other major areas of damage to the shape so i chose the two tanto route to make the most use of the steel...i certainly could have made this tanto a very slender shinogi-zukuri if i had wanted to tackle a shinogi-zukuri polish this summer though... ^______^

Share this post


Link to post
Share on other sites

I always love seeing your work, Dave-san!  And I'm sure you enjoyed the heck out of reforging that blade, the hada is very cool.  The chance to play with real tamahagane is all too rare to miss.

Share this post


Link to post
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!


Register a new account

Sign in

Already have an account? Sign in here.


Sign In Now