Aiden CC Posted May 8 Share Posted May 8 It’s a bit hard to tell, but it may be a bit high? If the sparks look good everywhere, my guess would be you might need a higher temperature and/or a faster quench. I would try a thinner coupon in water, and maybe shoot for a higher quench temperature than you are used to with modern steel. 1 Link to comment Share on other sites More sharing options...
Kreg Whitehead Posted May 8 Author Share Posted May 8 (edited) 37 minutes ago, Aiden CC said: It’s a bit hard to tell, but it may be a bit high? If the sparks look good everywhere, my guess would be you might need a higher temperature and/or a faster quench. I would try a thinner coupon in water, and maybe shoot for a higher quench temperature than you are used to with modern steel. Sounds good. I was mainly curious to see what if any patten I would have. Hopefully I can get some of this looking like a blade soon. Edited May 8 by Kreg Whitehead Link to comment Share on other sites More sharing options...
Recommended Posts
Create an account or sign in to comment
You need to be a member in order to leave a comment
Create an account
Sign up for a new account in our community. It's easy!
Register a new accountSign in
Already have an account? Sign in here.
Sign In Now